Giant magneto impedance effect in as-cast and post production treated Fe4.3Co68.2Si12.5B15 amorphous wires

Placeholder

Date

Organizational Units

Authors

Çaylak, Osman
Derebaşı, Naim

Authors

Advisor

Language

Publisher:

Amer Inst Physics

Journal Title

Journal ISSN

Volume Title

Abstract

Giant magneto impedance (GMI) effect is investigated on as-cast and post-production treated negative magnetostriction Fe4.3Co68.2Si12.5B15 amorphous wire with the diameter of 120 mu m and 12 cm long. As-cast, furnace annealed, furnace annealed under axial tension, dc current annealed and furnace annealed under transverse magnetic field samples were prepared for this investigation. The highest GMI ratio was found to be around 4 MHz for all samples. It is found to be the GMI effect sensitively depends on the post-production treated process, induced anisotropy and domain structures.

Description

Bu çalışma, 22-26, Ağustos 2006 tarihlerinde İstanbul[Türkiye]’de düzenlenen 6. International Conference of the Balkan-Physical-Union Kongresi‘nde bildiri olarak sunulmuştur.

Source:

Keywords:

Keywords

Amorphous magnetic materials, Physics

Citation

Çaylak, O. ve Derebaşı, N. (2007). "Giant magneto impedance effect in as-cast and post production treated Fe4.3Co68.2Si12.5B15 amorphous wires". AIP Conference Proceedings, 6. International Conference of the Balkan-Physical-Union, 899, 773-773.

Endorsement

Review

Supplemented By

Referenced By

0

Views

0

Downloads