Özet
In this research, the electrodeposition technique was employed to prepare fine-grained nickel, iron and iron-cobalt coatings with 1 pm thicknesses on the substrate of the Fe36Co36B19.2Si4.8Mo3W1 amorphous ribbons. The coating effect on magnetic properties was examined at room temperature using an ADE Magnetics EV9 vibrating sample magnetometer with maximum magnetic field strength of 1750 kA/m. It is found that Ni, Fe, and Fe-Co coated amorphous ribbons show 0.60, 0.71, and 1.01 T saturation magnetization, respectively, while uncoated ribbon has 1.55 T.
Açıklama
Bu çalışma, 24-28 Eylül 2013 tarihlerinde Antalya[Türkiye]’de düzenlenen 3. International Congress on Advances in Applied Physics and Materials Science Kongresi‘nde bildiri olarak sunulmuştur.
Kaynak:
Anahtar Kelimeler:
Konusu
Coatings, Iron research, Magnetic properties, Amorphous silicon, Nickel, Vibrating sample magnetometer, Silicon, Room temperature, Amorphous ribbon, Magnetic field strengths, Cobalt coating, Electrodeposition technique, Microstructure, Films, Physics
Alıntı
Perinçek, F. vd. (2014). "Coating effect on magnetic properties of Fe36Co 36B19:2Si4:8Mo3W1 amorphous ribbons". Acta Physica Polonica A, 3. International Congress on Advances in Applied Physics and Materials Science, 125(2), 408-410.