The effects of jacquard woven fabric constructional parameters and elastane yarn on bending rigidity

Abstract

In this research, the bending property of jacquard woven fabrics and the effects of weft density, weft yarn count, weave, and Lycra inclusion in weft yarn on this property were investigated. Viscose filament warp yarn and polyester and polyester/Lycra weft yarns were used for weaving fabrics, and 4/1 and 7/1 satin weaves with the same jacquard design were used as the ground weave. Experimental results show that the bending rigidities of the fabrics in the warp directions increase as the weft density increases and the weft yarn gets thicker. The bending rigidities of the fabrics woven with a 4/1 satin weave in the warp direction are higher compared to the bending rigidities of the fabrics woven with a 7/1 satin weave in the same direction. Similar to the bending rigidities in the warp direction, as the weft density increases and the weft yarn gets thicker, the bending rigidities of the fabrics in the weft directions increase. When the weft yarn includes Lycra, the bending rigidity values of the fabric decrease in the weft direction. Additionally, similar to the bending rigidity in the warp direction, the jacquard woven fabrics with a 4/1 satin weave have a higher bending rigidity in the weft direction compared to the jacquard woven fabrics with a 7/1 satin weave. It was observed that when the weft density increases, the overall bending rigidities of the fabrics increase. Despite fabrics woven with a polyester/Lycra weft yarn having a thicker weft yarn and heavier weight with the same weft density and weave compared to fabrics woven with a polyester weft yarn, the bending rigidity values in the weft direction have a lower overall fabric bending rigidity.