304 paslanmaz çeliğinin kaynak yoluyla St 37 çeliği ile birleştirilmesi ve mekanik özelliklerinin incelenmesi
Files
Date
2006
Authors
Journal Title
Journal ISSN
Volume Title
Publisher
Uludağ Üniversitesi
Abstract
Bu çalışmada st37 çeliği ile 304 paslanmaz çeliğinin birbirine MAG kaynağıyla birleştirilmesi ve oluşan kaynak dikişinin sıcaklık ve zaman ile değişen mekanik özellikleri incelenmiştir. İncelemeler sonucu en yüksek kopma mukavemet değeri difüzyon ve Krom – Karbür çökelmesi sebebiyle ısıl işlem uygulanmamış parçada bulunmuş (64,53 DaN/mm2 ) en düşük kopma mukavemeti ise 450°C de 4 saat bekletilmiş parçada elde edilmiştir (44,96 DaN/mm2 ). En yüksek sertlik değeri ise 450°C de 4 saat bekletilmiş parçada elde edilmiştir (547 HV)
In this study St37 and 304 steels are welded with MAG welding method. Changing mechanical properties of welded area under high temperatures and time is researched. According to the results the highest tensile strength value was determined on the piece that was not treated with heat (64,53 DaN/mm2 ) and the lowest tensile strength value was determined on the piece that had been kept under 450°C for 4 hours (44,96 DaN/mm2 ). The highest hardness value was determined in the piece that had been kept under 450°C for 4 hours (547 HV).
In this study St37 and 304 steels are welded with MAG welding method. Changing mechanical properties of welded area under high temperatures and time is researched. According to the results the highest tensile strength value was determined on the piece that was not treated with heat (64,53 DaN/mm2 ) and the lowest tensile strength value was determined on the piece that had been kept under 450°C for 4 hours (44,96 DaN/mm2 ). The highest hardness value was determined in the piece that had been kept under 450°C for 4 hours (547 HV).
Description
Keywords
St37, 304 paslanmaz çeliği, Uyumsuz metallerin kaynak özellikleri, 304 stainless steel, Welding properties of incompatible metals
Citation
Baran, E. E. (2006). 304 paslanmaz çeliğinin kaynak yoluyla St 37 çeliği ile birleştirilmesi ve mekanik özelliklerinin incelenmesi. Yayınlanmamış yüksek lisans tezi. Uludağ Üniversitesi Fen Bilimleri Enstitüsü.