  • No Thumbnail Available
    Item
    Investigation of TiO2 thin films as a cathodic material for electrochromic display devices
    (Springer, 2020-04-26) Akkurt, Nihan; Pat, Suat; Mohammadigharehbagh, Reza; Özgür, Mustafa; Demirkol, Uğur; Korkmaz, Sadan; Olkun, Ali; Bursa Uludağ Üniversitesi/Fen-Edebiyat Fakültesi/Fizik Bölümü.; DJH-5166-2022; 57216253716
    Titanium dioxide is a preferred material in many fields of applications and is also used as one of best electrochromic display (ECD) candidates due to its chemical stability. Electrochromic devices are innovative, low-cost and low energy consumption for using as displays. In this work, electrochromic, morphological, structural, and some optical properties of tandem structures were comprehensively investigated. The mean thicknesses of the samples were measured as 86 and 120 nm on ITO- and FTO-coated glass substrates, respectively. The chronoamperometry test was performed to determine some electrochromic properties of the ECD. It was observed that the amounts of ions intercalated/de-intercalated from the coated TiO2 layer were almost equal to each other. According to the chronocoulometric analysis, the superior reversibility and coloration efficiency of the assembled ECD were found to be 83% and 26 cm(2)/C, respectively, onto ITO substrates. Higher reversibility is revealed in thinner films, which is consistent with the obtained thickness results. In a similar manner, highest coloration efficiency obtained for our ECD has demonstrated good contact between the TiO2-deposited layer and the ITO-coated glass substrate. Also, the highest porosity was reached by taking the highest coloration efficiency value into account. Moreover, coloration efficiencies and Delta T ratios are changed due to the interlayer transparent conductive oxide layers. Raman spectroscopy measurement reveals the anatase phase of TiO2 films on both substrates. Another important finding is related to the defect structures of the TiO2 phase. TiO2, TiO3 and TiO4 mixed phases show the lower coloration efficiency according to the TiO2 phase, for the first time. TiO3 and TiO4 phases were grown by using the FTO-coated glass substrate. Comparing results with reports has shown that our investigated design and technology for ECD applications are good candidates for such applications.
  • No Thumbnail Available
    Publication
    Substrate effect on electrochromic properties of Nb2O5:TiO2 nanocomposite thin films deposited by thermionic vacuum arc
    (Pergamon-elsevier Science Ltd, 2022-05-21) Özgür, Nihan Akkurt; Pat, Suat; Korkmaz, Sadan; Mohammadigharehbagh, Reza; Bursa Uludağ Üniversitesi/Fen Edebiyat Fakültesi/Fizik Anabilim Dalı.; 0000-0002-0333-487X; 0000-0003-0116-3795
    In this paper, substrate effect on electrochromic properties of Nb2O5:TiO2 nanocomposite thin films have been investigated. Thin films have been deposited by thermionic vacuum arc deposition technology. Nb2O5 and TiO2 are known to be electrochromic materials. Nb/Ti rate was obtained 1.4. Average thicknesses of the films were found as 113 nm and 111 nm and band gap values for bleached states were calculated as 3.96 eV and 3.85 eV for the films deposited onto ITO and FTO coated glass substrates, respectively. The coloration efficiency values were calculated as 17 cm2/C and 26 cm2/C for the film onto ITO layered glass substrate and 31 cm2/C, 23 cm2/C and 24 cm2/C for the film onto FTO layered glass substrate at a different wavelength values in the visible region. The obtained results shows that films for each transparent conductive oxide material is promising material to obtain the high performance TiO2 active layer.