Yıldırım, Kenan2022-03-082022-03-082009Yıldırım, K. vd. (2009). "The effect of first heater temperature on the properties of false-twist textured poly (ethylene terapthalate) yarn". Tekstil ve Konfeksiyon, 19(4), 286-290.1300-3356https://dergipark.org.tr/tr/download/article-file/218134http://hdl.handle.net/11452/24883The effect of First heater temperature on the properties of poly (ethylene terapthalate) filaments was characterized through, I measurements of tenacity, breaking elongation, boiling shrinkage, crimp stability, crimp contraction and crystallinity. It Wits found that crystallinity reached a maximum at a temperature around 200 C, and then started to decrease. A similar behavior was observed in crimp stability. Tenacity and crimp contraction increased and boiling water shrinkage decreased, when the heater temperature increased.Birinci fırın sıcaklığının polietilen teraftalat filamentlerin özelliklerine etkisi kopma mukavemeti, kopma uzaması, kaynama çekmesi, kıvrım stabilitesi, kıvrım büzülmesi ve kristalinite ölçümleriyle incelenmiştir. Kristalinitenin 200oC civarında maksimuma ulaştığı ve ardından düşmeğe başladığı bulunmuştur. Kıvrım stabilitesinde de benzer bir davranış gözlenmiştir. Isıtıcı sıcaklığı arttığında kopma mukavemeti ve kıvrım büzülmesi artmış, kaynama çekmesi ise düşmüştür.eninfo:eu-repo/semantics/openAccessFalse-twist texturingHeater temperatureStructure-propertiesTexturingPolyethylene terephthalate yarnMaterials scienceYalancı bükümlü tekstureFırın sıcaklığıYapı-özellikTekstureThe effect of first heater temperature on the properties of false-twist textured poly (ethylene terapthalate) yarnBirinci fırın sıcaklığının yalancı bükümle tekstüre edilen polietilen teraftalat ipliklerinin özelliklerine etkisiArticle0002736002000062-s2.0-84858667763286290194Materials science, textilesFalse Twist; Texturing Machine; Finite Element Analysis