dc.identifier.citationGüneş, Ş. (2014). Polimer ince filmlerin manyetik özelliklerinin araştırılması. Yayınlanmamış yüksek lisans tezi. Uludağ Üniversitesi Fen Bilimleri Enstitüsü.tr_TR
dc.identifier.urihttp://hdl.handle.net/11452/5509-
dc.description.abstractBu tezde, üç farklı polimer içerisine katkılanan baryum ferrit (BF) nano parçacıkların yapısal, elektriksel ve manyetik özellikleri incelenmiştir. Yapısal incelemelerde XRD ve AFM, elektriksel incelemelerde I-V ve C-V ölçümleri ve manyetik incelemelerde ise VSM ve MFM teknikleri kullanılmıştır. Yapısal incelemelerde, baryum ferrit katkılı polimer ince filmlerin çok küçük kristal boyutlarına sahip oldukları belirlenmiştir. Yapılan AFM ölçümlerinde ise polimer filmlerin yüzey pürüzlülük değerlerinin 16 nm ile 240 nm arasında değiştiği gözlemlenmiştir. En düşük yüzey pürüzlülük değeri P(VA)-BF örneğinde elde edilmiştir. Elektriksel ölçümler oda sıcaklığında gerçekleştirilmiştir. Ortalama engel yüksekliği akım-gerilim ölçümlerinden 0,68±0,02 eV, kapasitans-gerilim ölçümlerinden de 0,75±0,02 eV olarak elde edilmiştir Polimer filmlerin VSM ölçümlerinden histeresis eğrileri elde edilmiştir. Histeresis eğrileri incelendiğinde polimer filmlerin ferromanyetik özellik gösterdikleri görülmektedir. En yüksek doyum mıknatıslanma değerine sahip örnek P(VA)-BF olarak ölçülmüştür. MFM resimlerinde gözlenen parlak ve mat bölgeler mıknatıslanma yönlerini belirtmektedir.tr_TR
dc.description.abstractIn this thesis, the structural, electrical and magnetic properties of three different type polymer films doped with barium ferrite nano particles have been investigated. XRD and AFM techniques were used for structural investigations. I-V and C-V measurements were used for electrical investigations and VSM and MFM were used for investigation of magnetic properties. In structural investigations, polymer films doped with barium ferrite have a very small crystalline size. The AFM results showed that the range of the polymer films surface roughness value is between 16 nm and 240 nm. The lowest surface roughness value was obtained in P(VA)-BF. Electrical measurements were carried out at room temperature. The average barriers heights of 0,68±0,02 eV and 0,75±0,02 eV was obtained from current-voltage and capacitance-voltage measurements, respectively. The hysteresis curves of the polymer films were obtained by VSM measurement. As can be seen from hysteresis curves, polymer films show ferromagnetic behavior. The highest saturation magnetization value was measured in P(VA)-BF. The bright and dark areas in MFM image is represented magnetization direction.en_US
dc.format.extentIX, 49 sayfatr_TR
dc.language.isotrtr_TR
dc.publisherUludağ Üniversitesitr_TR
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.rightsAtıf 4.0 Uluslararasıtr_TR
dc.rights.urihttp://creativecommons.org/licenses/by/4.0/*
dc.subjectPolimerlertr_TR
dc.subjectBaryum ferrittr_TR
dc.subjectManyetik özelliklertr_TR
dc.subjectNano yapılartr_TR
dc.subjectPolymersen_US
dc.subjectBarium ferriteen_US
dc.subjectMagnetic propertiesen_US
dc.subjectNanoparticlesen_US
dc.titlePolimer ince filmlerin manyetik özelliklerinin araştırılmasıtr_TR
dc.title.alternativeInvestigation of magnetic properties of polymer thin filmsen_US
dc.typemasterThesisen_US
dc.relation.publicationcategoryTeztr_TR
dc.contributor.departmentUludağ Üniversitesi/Fen Bilimleri Enstitüsü/Fizik Anabilim Dalı.tr_TR
Appears in Collections:Yüksek Lisans Tezleri / Master Degree

Files in This Item:
File Description SizeFormat 
360506.pdf2.76 MBAdobe PDFThumbnail
View/Open


This item is licensed under a Creative Commons License Creative Commons